Standard Specification for Metallic-Coated Steel Wire for Chain-Link Fence Fabric and Marcelled Tension Wire

This specification covers metallic-coated carbon steel wire for the manufacture of chain-link fence fabric and marcelled tension wire. Three coating types, namely: Type I (aluminized), Type II (galvanized), and Type III (zinc-aluminum-mischmetal alloy-coated), and five coating classes, namely: Class 3, Class 4, Class 5, Class 60, and Class 100, are covered. This specification does not cover the wire for chain-link fence when the coating is to be applied after the weaving process. The steel rod from which the wire is to be drawn shall be manufactured by the open-hearth, electric-furnace, or basic-oxygen process. The wire shall be cold-drawn, then metallic-coated at finished size to produce the specified mechanical properties such as breaking strength. Type I and Type III coatings shall be produced by a hot-dip process and Type II coating by either a hot-dip or an electrolytic process. The ingot or pig aluminum to be used for Type I coating shall conform to the impurity limits specified for copper and iron. Requirements for coated wire diameter, coating weight, coating adherence, and methods of chemical analysis and breaking strength test are detailed.

Informations générales

Collections

Normes américaines ASTM

Date de publication

août 2017

Nombre de pages

0 p.

Référence

ASTM A817-12(2017)

Indice de classement

A0817-12R17
Résumé
Standard Specification for Metallic-Coated Steel Wire for Chain-Link Fence Fabric and Marcelled Tension Wire

This specification covers metallic-coated carbon steel wire for the manufacture of chain-link fence fabric and marcelled tension wire. Three coating types, namely: Type I (aluminized), Type II (galvanized), and Type III (zinc-aluminum-mischmetal alloy-coated), and five coating classes, namely: Class 3, Class 4, Class 5, Class 60, and Class 100, are covered. This specification does not cover the wire for chain-link fence when the coating is to be applied after the weaving process. The steel rod from which the wire is to be drawn shall be manufactured by the open-hearth, electric-furnace, or basic-oxygen process. The wire shall be cold-drawn, then metallic-coated at finished size to produce the specified mechanical properties such as breaking strength. Type I and Type III coatings shall be produced by a hot-dip process and Type II coating by either a hot-dip or an electrolytic process. The ingot or pig aluminum to be used for Type I coating shall conform to the impurity limits specified for copper and iron. Requirements for coated wire diameter, coating weight, coating adherence, and methods of chemical analysis and breaking strength test are detailed.

Besoin d’identifier, de veiller et de décrypter les normes ?

COBAZ est la solution simple et efficace pour répondre aux besoins normatifs liés à votre activité, en France comme à l’étranger.

Disponible sur abonnement, CObaz est LA solution modulaire à composer selon vos besoins d’aujourd’hui et de demain. Découvrez vite CObaz !

Demandez votre démo live gratuite, sans engagement

Je découvre COBAZ