This specification covers the standard requirements for semi-processed cold-rolled magnetic lamination quality steels. These steels shall be made by the basic-oxygen or electric-furnace method and shall be processed by hot rolling, pickling, cold rolling, annealing, and temper rolling. Magnetic lamination steels shall have low-carbon contents and may have manganese, phosphorus, silicon, and aluminum additions to enhance punchability and to improve magnetic characteristics by increasing the electrical resistivity. There are no fixed chemical requirements for these steels only the requirement to meet the specified magnetic properties. These steels must be heat treated by the user to develop the specified magnetic properties. This specification covered steels with thicknesses of 0.0185 in. ( 0.47 mm), 0.022 in. (0.56 mm), 0.025 in. (0.64 mm), 0.028 in. (0.71 mm) and 0.031 in. (0.79 mm). For a given thickness there are three or more core loss types distinguished by maximum allowable core loss after a specified quality development anneal. Magnetic testing shall be done after the specified quality development anneal and shall use the Epstein test method. Magnetic testing shall be done at a test frequency of 60 Hz and a maximum flux density of 15 kG (1.5 T). Test methods to determine the magnetic and mechanical properties are listed. Other typical magnetic and physical properties are listed for reference.
This specification covers the standard requirements for semi-processed cold-rolled magnetic lamination quality steels. These steels shall be made by the basic-oxygen or electric-furnace method and shall be processed by hot rolling, pickling, cold rolling, annealing, and temper rolling. Magnetic lamination steels shall have low-carbon contents and may have manganese, phosphorus, silicon, and aluminum additions to enhance punchability and to improve magnetic characteristics by increasing the electrical resistivity. There are no fixed chemical requirements for these steels only the requirement to meet the specified magnetic properties. These steels must be heat treated by the user to develop the specified magnetic properties. This specification covered steels with thicknesses of 0.0185 in. ( 0.47 mm), 0.022 in. (0.56 mm), 0.025 in. (0.64 mm), 0.028 in. (0.71 mm) and 0.031 in. (0.79 mm). For a given thickness there are three or more core loss types distinguished by maximum allowable core loss after a specified quality development anneal. Magnetic testing shall be done after the specified quality development anneal and shall use the Epstein test method. Magnetic testing shall be done at a test frequency of 60 Hz and a maximum flux density of 15 kG (1.5 T). Test methods to determine the magnetic and mechanical properties are listed. Other typical magnetic and physical properties are listed for reference.
This specification covers the standard requirements for semi-processed cold-rolled magnetic lamination quality steels. These steels shall be made by the basic-oxygen or electric-furnace method and shall be processed by hot rolling, pickling, cold rolling, annealing, and temper rolling. Magnetic lamination steels shall have low-carbon contents and may have manganese, phosphorus, silicon, and aluminum additions to enhance punchability and to improve magnetic characteristics by increasing the electrical resistivity. There are no fixed chemical requirements for these steels only the requirement to meet the specified magnetic properties. These steels must be heat treated by the user to develop the specified magnetic properties. This specification covered steels with thicknesses of 0.0185 in. ( 0.47 mm), 0.022 in. (0.56 mm), 0.025 in. (0.64 mm), 0.028 in. (0.71 mm) and 0.031 in. (0.79 mm). For a given thickness there are three or more core loss types distinguished by maximum allowable core loss after a specified quality development anneal. Magnetic testing shall be done after the specified quality development anneal and shall use the Epstein test method. Magnetic testing shall be done at a test frequency of 60 Hz and a maximum flux density of 15 kG (1.5 T). Test methods to determine the magnetic and mechanical properties are listed. Other typical magnetic and physical properties are listed for reference.
COBAZ est la solution simple et efficace pour répondre aux besoins normatifs liés à votre activité, en France comme à l’étranger.
Disponible sur abonnement, CObaz est LA solution modulaire à composer selon vos besoins d’aujourd’hui et de demain. Découvrez vite CObaz !
Demandez votre démo live gratuite, sans engagement
Je découvre COBAZ