1.1 This specification covers stainless steel wire, except the free-machining types. It includes round, square, octagon, hexagon, and shape wire in coils only for the more commonly used types of stainless steels for general corrosion resistance and high-temperature service. For bars in straightened and cut lengths, see Specifications A276 or A479/A479M.

Note 1: For free-machining stainless wire, designed especially for optimum machinability, see Specification A581/A581M.

1.2 Unless the order specifies the applicable “M” specification designation, the material shall be furnished to the inch-pound units.

1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

Main informations

Collections

ASTM american standards

Publication date

February 2018

Number of pages

0 p.

Reference

ASTM A580/A580M-18

Classification index

A0580_A0580M-18

Sumary

Standard Specification for Stainless Steel Wire

This specification covers stainless steel wire, except the free-machining types. It includes round, square, octagon, hexagon, and shape wire in coils only for the more commonly used types of stainless steels for general corrosion resistance and high-temperature service. The steel specimens shall undergo the following conditions: (1) annealed as a final heat treatment; (2) cold worked to higher strength; (3) heat treated to an intermediate temper; or (4) heat treated to a hard temper by austenitizing, quenching, and tempering at a relatively low temperature. The materials shall be cold drawn, annealed, and pickled. The steel wires shall conform to the required chemical compositions of carbon, manganese, phosphorus, sulfur, silicon, chromium, nickel, molybdenum, nitrogen, and other elements such as niobium , vanadium, copper, tantalum, titanium and cobalt. Mechanical test shall be performed wherein in the steel specimens shall conform to the required values of tensile strength, yield strength, and elongation. The martensitic grades shall conform to the required values of hardness after heat treatment.

Replaced standards (1)

ASTM A580/A580M-16

September 2016

Standard Cancelled

Standard Specification for Stainless Steel Wire

This specification covers stainless steel wire, except the free-machining types. It includes round, square, octagon, hexagon, and shape wire in coils only for the more commonly used types of stainless steels for general corrosion resistance and high-temperature service. The steel specimens shall undergo the following conditions: (1) annealed as a final heat treatment; (2) cold worked to higher strength; (3) heat treated to an intermediate temper; or (4) heat treated to a hard temper by austenitizing, quenching, and tempering at a relatively low temperature. The materials shall be cold drawn, annealed, and pickled. The steel wires shall conform to the required chemical compositions of carbon, manganese, phosphorus, sulfur, silicon, chromium, nickel, molybdenum, nitrogen, and other elements such as niobium , vanadium, copper, tantalum, titanium and cobalt. Mechanical test shall be performed wherein in the steel specimens shall conform to the required values of tensile strength, yield strength, and elongation. The martensitic grades shall conform to the required values of hardness after heat treatment.

Standard replaced by (1)

ASTM A580/A580M-23

May 2023

Standard Current

Standard Specification for Stainless Steel Wire

This specification covers stainless steel wire, except the free-machining types. It includes round, square, octagon, hexagon, and shape wire in coils only for the more commonly used types of stainless steels for general corrosion resistance and high-temperature service. The steel specimens shall undergo the following conditions: (1) annealed as a final heat treatment; (2) cold worked to higher strength; (3) heat treated to an intermediate temper; or (4) heat treated to a hard temper by austenitizing, quenching, and tempering at a relatively low temperature. The materials shall be cold drawn, annealed, and pickled. The steel wires shall conform to the required chemical compositions of carbon, manganese, phosphorus, sulfur, silicon, chromium, nickel, molybdenum, nitrogen, and other elements such as niobium , vanadium, copper, tantalum, titanium and cobalt. Mechanical test shall be performed wherein in the steel specimens shall conform to the required values of tensile strength, yield strength, and elongation. The martensitic grades shall conform to the required values of hardness after heat treatment.

What is the Redline format?

The Redline + service - standards comparator allows you to easily and simply identify major changes between the current standard and its last canceled version.

At a glance, you will be able to identify the additions, deletions or modifications to a text, table, figure and formula.

At a glance, you will be able to identify the additions, deletions or modifications to a text, table, figure and formula

The Redlines + service is offered to you on the collection of French standards in force, in French language and in HTML and PDF format.

For an overview of the service, click on View a standard in redline format

Need to identify, monitor and decipher standards?

COBAZ is the simple and effective solution to meet the normative needs related to your activity, in France and abroad.

Available by subscription, CObaz is THE modular solution to compose according to your needs today and tomorrow. Quickly discover CObaz!

Request your free, no-obligation live demo

I discover COBAZ