ASTM B196/B196M-24

ASTM B196/B196M-24

June 2024
Standard Current

Standard Specification for Copper-Beryllium Alloy Rod and Bar

This specification establishes the requirements for rods and bars in straight lengths of copper-beryllium alloys with Copper Alloy UNS Nos. C17000, C17200, and C17300. The material for manufacture shall be cast and worked to such purity and soundness as to be suitable for processing by hot working, cold working, and annealing to produce a uniform wrought structure and specified temper in the finished product. Products shall be available in the following tempers: solution heat-treated TB00 (A), and cold-drawn hard TD04 (H), which shall be precipitation heat treated after machining or forming. Products that are already precipitation heat treated by the manufacturer shall be available in tempers TF00 (AT) and TH04 (HT). Products shall be sampled and prepared, then tested accordingly to examine their conformance to dimensional (diameter, length, straightness, and edge contour), mechanical (tensile and yield strength, Rockwell hardness, and elongation), and chemical composition requirements.

See more
Additional informations

1.1 This specification covers the requirements for Copper Alloy UNS Nos. C17000. C17200, and C17300 rod and bar in straight lengths.

1.2 Unless otherwise specified in the contract or purchase order, Copper Alloy UNS No. C17200 shall be the alloy furnished.

1.3 The values stated in either inch-pounds or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.

1.4 The following safety hazard caveat pertains only to the test methods described in this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.


Main informations

Collections

ASTM american standards

Publication date

June 2024

Number of pages

0 p.

Reference

ASTM B196/B196M-24

Classification index

B0196_B0196M-24
Sumary
Standard Specification for Copper-Beryllium Alloy Rod and Bar

This specification establishes the requirements for rods and bars in straight lengths of copper-beryllium alloys with Copper Alloy UNS Nos. C17000, C17200, and C17300. The material for manufacture shall be cast and worked to such purity and soundness as to be suitable for processing by hot working, cold working, and annealing to produce a uniform wrought structure and specified temper in the finished product. Products shall be available in the following tempers: solution heat-treated TB00 (A), and cold-drawn hard TD04 (H), which shall be precipitation heat treated after machining or forming. Products that are already precipitation heat treated by the manufacturer shall be available in tempers TF00 (AT) and TH04 (HT). Products shall be sampled and prepared, then tested accordingly to examine their conformance to dimensional (diameter, length, straightness, and edge contour), mechanical (tensile and yield strength, Rockwell hardness, and elongation), and chemical composition requirements.

Replaced standards (1)
ASTM B196/B196M-18
March 2018
Standard Cancelled
Standard Specification for Copper-Beryllium Alloy Rod and Bar

This specification establishes the requirements for rods and bars in straight lengths of copper-beryllium alloys with Copper Alloy UNS Nos. C17000, C17200, and C17300. The material for manufacture shall be cast and worked to such purity and soundness as to be suitable for processing by hot working, cold working, and annealing to produce a uniform wrought structure and specified temper in the finished product. Products shall be available in the following tempers: solution heat-treated TB00 (A), and cold-drawn hard TD04 (H), which shall be precipitation heat treated after machining or forming. Products that are already precipitation heat treated by the manufacturer shall be available in tempers TF00 (AT) and TH04 (HT). Products shall be sampled and prepared, then tested accordingly to examine their conformance to dimensional (diameter, length, straightness, and edge contour), mechanical (tensile and yield strength, Rockwell hardness, and elongation), and chemical composition requirements.

What is the Redline format?
The Redline + service - standards comparator allows you to easily and simply identify major changes between the current standard and its last canceled version.

At a glance, you will be able to identify the additions, deletions or modifications to a text, table, figure and formula.
At a glance, you will be able to identify the additions, deletions or modifications to a text, table, figure and formula

The Redlines + service is offered to you on the collection of French standards in force, in French language and in HTML and PDF format.

For an overview of the service, click on View a standard in redline format
Need to identify, monitor and decipher standards?

COBAZ is the simple and effective solution to meet the normative needs related to your activity, in France and abroad.

Available by subscription, CObaz is THE modular solution to compose according to your needs today and tomorrow. Quickly discover CObaz!

Request your free, no-obligation live demo

I discover COBAZ