ISO 3211:2010 specifies an empirical method for assessing the resistance of anodic oxidation coatings to cracking by deformation. The method is applicable particularly to sheet material with anodic oxidation coatings of thickness less than 5 µm, and is useful for development purposes.
ISO 3211:2010 specifies an empirical method for assessing the resistance of anodic oxidation coatings to cracking by deformation.
The method is applicable particularly to sheet material with anodic oxidation coatings of thickness less than 5 µm, and is useful for development purposes.
Le présent document décrit une méthode de contrôle empirique permettant d'évaluer la résistance des couches anodiques à la formation de criques par suite de déformations que peuvent subir ces couches.
<p>This document specifies an empirical method for assessing the resistance of anodic oxidation coatings to cracking by deformation.</p> <p>The method is applicable particularly to sheet material with anodic oxidation coatings of thickness less than 5 µm, and is useful for development purposes.</p> <p>NOTE If the test specimen is thick, more than 5 µm of coating can be measured (see Clause 9).</p>
COBAZ is the simple and effective solution to meet the normative needs related to your activity, in France and abroad.
Available by subscription, CObaz is THE modular solution to compose according to your needs today and tomorrow. Quickly discover CObaz!
Request your free, no-obligation live demo
I discover COBAZ